Technical specifications
| Application | ||
|---|---|---|
| Automotive Grips | Automotive-HVAC Flapper Door Seals | Automotive-Interior |
| Consumer –Electronics | Consumer-Floor Care | Consumer- Kitchen |
| Seals and gaskets | Building & Construction | Tools |
| Uses | ||
|---|---|---|
| Application Components | Appliances | Automotive Applications |
| Bonding | Cell phones | Consumer Applications |
| White Goods & Small Appliances | Strain Reliefs | Flexible Grips |
| Kitchenware | Living Hinges | Seals |
| Sporting Goods | Tie –Layer | |
| ROHS Compliance | ROHS Compliant |
|---|---|
| Process method | Extrusion & Co –Extrusion |
Basic Raw Material Properties
| Hardness | Value | Test Reference |
|---|---|---|
| Shore Hardness Shore A , 15 Sec , 730 F ( 230 C) |
53 | ISO 868 |
| Elastomers | Value | Test Reference |
|---|---|---|
| Elongation at Break –Across Flow 730 F ( 230 C) |
600 % | ASTM D412 |
| Tensile Strain at Break –Across Flow 730 F ( 230 C) |
600 % | ISO 37 |
| Compression Set 2570 F ( 1250 C),70 hr ,Type1 |
55% | ASTM D395B |
| Compression Set 2570 F ( 1250 C),70 hr ,Type A |
55% | ISO 815 |
| Ageing | Value | Test Reference |
|---|---|---|
| Change in Tensile strength Air 2120 F ( 1000 C),168 HR 2570 F ( 1250 C),168 HR |
-28% | ASTM D573/ISO 188 |
| Change in Ultimate Elongation in Air 2120 F ( 1000 C),168 HR 2570 F ( 1250 C),168 HR |
14 % -70 % |
ASTM D573 |
| Change in Tensile Strain at Break in Air 2120 F ( 1000 C),168 HR 2570 F ( 1250 C),168 HR |
-14 % -70 % |
ISO 188 |
| Change in Durometer Hardness in Air 2120 F ( 1000 C),168 HR 2570 F ( 1250 C),168 HR |
-4.0 8 |
ASTM D573 |
| Change in Shore Hardness in Air 2120 F ( 1000 C),168 HR 2570 F ( 1250 C),168 HR |
-4.0 8 |
ISO 188 |
| Flammability | Value | Test Reference |
|---|---|---|
| Flame Rating | UL 94 | |
| 0.04 in (1.1 mm) | HB | |
| 0.11 in ( 2.9 mm) | HB |